DELO MONOPOX 1197 Construction Adhesive TDS

DELOMONOPOX® 1197

heat curing, construction adhesive

Base

–   epoxy resin, construction adhesive

–   one-component, heat-curing, filled

Use

–   for the bonding of all metal types, temperature-resistant plastic, ferrite and ceramic

–   especially for high-strength, tough-hard bondings with very high static and dynamic loading capacity, even at increased temperatures

–   for bondings requiring a high run resistance

–   the product is normally used in a temperature range of -55 °C to +200 °C; depending on the application, other limits may be more reasonable

–   compliant with RoHS directive 2002/95/EC

Processing

–   to heat the components, increased temperatures can be used, as well

–   the heating time of the components must be added to the actual curing time

–   for curing, the inside of the adhesive layer must have the required temperature

–   depending on the adhesive amount used, exothermic reaction heat is developed which can lead to overheating; in this case, the curing temperature must be reduced accordingly

–   the adhesive is supplied ready for use and can be processed well from the original container or with DELO dispensing units

–   the surfaces to be bonded must be dry as well as free of dust, grease and other contaminations

–   use DELOTHEN cleaners for the cleaning of bonding surfaces

–   adhesion to the components can be improved by sand blasting, grinding or pickling

Curing

–   curing proceeds at temperatures between +130 and +180 °C

–   increased temperatures shorten the curing process, lower temperatures extend it, and can change the properties of the cured product

Technical data
Color                                                                                                               silver grey
Filler                                                                                                               aluminum
Density [g/cm³]  at room temperature (approx. 23 °C)              1.4
Viscosity [mPas] at 23 °C, Brookfield rpm 7/5                               pasty
Processing time   at room temperature (max. 25 °C)                   6 weeks

Curing time until final strength [min]                                                 75
at 130°C in a convection oven
Curing time until final strength [min]                                                 40
at 150 °C in an air convection oven
Curing time until final strength [min]                                                  15
at 180 °C in an air convection oven
Tensile shear strength Al/Al [MPa]                                                       26
DIN EN 1465, sand-blasted
component thickness: 1.6 mm
after 40 min at +150 °C
Tensile shear strength Al/Al [MPa]                                                       55
DELO Standard 39, sand-blasted
component thickness: 6 mm
after 40 min at +150 °C

Floating roller peel resistance St/St [N/mm]                                   12
DELO Standard 38, sand-blasted
component thickness: 1.5 mm
Temperature stability Al/Al at +50 °C [MPa]                                   33
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mmm
Temperature stability Al/Al at +100 °C [MPa]                                 22
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mm
Temperature stability Al/Al at +150 °C [MPa]                                 5
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mm

Tensile strength [MPa]                                                                                 40
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Elongation at tear [%]                                                                                    1.4
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Young’s modulus [MPa]                                                                                3300
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Shore hardness D                                                                                             67
according to DIN EN ISO 868
after 40 min at +150 °C
Decomposition temperature [°C]                                                             280
DELO Standard 36
Ball indentation hardness [MPa]                                                                95
ISO 2039, part 1
Glass transition temperature [°C]                                                              140
rheometer
Coefficient of linear expansion [ppm/K]                                                   93
TMA, in a temperature range of +25 to +140 °C
Coefficient of linear expansion [ppm/K]                                                   65
TMA, in a temperature range of +30 to +90 °C
Coefficient of linear expansion [ppm/K]                                                    171
TMA, in a temperature range of +130 to +150 °C
Shrinkage [vol. %]                                                                                                 3.0
DELO Standard 13
Water absorption [weight %]                                                                            0.1
according to DIN EN ISO 62
after 40 min at +150 °C
Dielectric strength [kV/mm]                                                                               2

VDE 0303, part 2, after 40 min at +150 °C
Dielectric constant                                                                                                   3.6
VDE 0303, part 4, after 40 min at +150 °C
Creep resistance CTI                                                                                                125M
VDE 0303, part 1, IEC 112, after 40 min at +150 °C
Storage life at 0 °C to +8 °C                                                                                     6 months
in unopened original container

Instructions and advice

General

The data and information provided are based on tests performed under laboratory conditions. Reliable information about the behavior of the product under practical conditions and its suitability for a specific purpose cannot be concluded from this.

Many product properties are subject to temperature and may change permanently, especially at high temperatures.

It is the user’s responsibility to test the suitability of the product for the intended purpose and temperature range of use by considering all specific requirements. Type and physical and chemical properties of the materials to be processed with the product, as well as all actual influences occurring during transport, storage, processing and use, may cause deviations in the behavior of the product

compared to its behavior under laboratory conditions. All data provided are typical average values or uniquely determined parameters

measured under laboratory conditions.

The data and information provided are, therefore, no guarantee for specific product properties or the suitability of the product for a specific purpose.

Instructions for use

The instructions for use of DELOMONOPOX are available on: www.DELO.de. We will be pleased to send them to you on demand.

Occupational health and safety

see material safety data sheet

Specification

see quality assurance test report

 

华为网盘下载: http://dl.dbank.com/c0kpy24m9x

注册本地下载:

  DELO_MONOPOX_1197 (167.0 KB, 6 次)
您没有权限下载此文件。

豆瓣 腾讯微博 QQ空间 新浪微博

电子胶水达人!

    联系站长

    • Name:QiuBo QQ:1808976
      Email:Anndiqiu#Gmail.com
      Mobile Phone:13923499497

    热门文章

    添加站长微信,与站长在线实时交流

    QQ不在线时请用微信

    最近评论

    • 正在加载...

    轻量、专注的消息,关注电子胶粘剂、电子胶水、电子制造工艺及设备产品的新鲜资讯。

链接