DELOMONOPOX® 1197
heat curing, construction adhesive
Base
– epoxy resin, construction adhesive
– one-component, heat-curing, filled
Use
– for the bonding of all metal types, temperature-resistant plastic, ferrite and ceramic
– especially for high-strength, tough-hard bondings with very high static and dynamic loading capacity, even at increased temperatures
– for bondings requiring a high run resistance
– the product is normally used in a temperature range of -55 °C to +200 °C; depending on the application, other limits may be more reasonable
– compliant with RoHS directive 2002/95/EC
Processing
– to heat the components, increased temperatures can be used, as well
– the heating time of the components must be added to the actual curing time
– for curing, the inside of the adhesive layer must have the required temperature
– depending on the adhesive amount used, exothermic reaction heat is developed which can lead to overheating; in this case, the curing temperature must be reduced accordingly
– the adhesive is supplied ready for use and can be processed well from the original container or with DELO dispensing units
– the surfaces to be bonded must be dry as well as free of dust, grease and other contaminations
– use DELOTHEN cleaners for the cleaning of bonding surfaces
– adhesion to the components can be improved by sand blasting, grinding or pickling
Curing
– curing proceeds at temperatures between +130 and +180 °C
– increased temperatures shorten the curing process, lower temperatures extend it, and can change the properties of the cured product
Technical data
Color silver grey
Filler aluminum
Density [g/cm³] at room temperature (approx. 23 °C) 1.4
Viscosity [mPas] at 23 °C, Brookfield rpm 7/5 pasty
Processing time at room temperature (max. 25 °C) 6 weeks
Curing time until final strength [min] 75
at 130°C in a convection oven
Curing time until final strength [min] 40
at 150 °C in an air convection oven
Curing time until final strength [min] 15
at 180 °C in an air convection oven
Tensile shear strength Al/Al [MPa] 26
DIN EN 1465, sand-blasted
component thickness: 1.6 mm
after 40 min at +150 °C
Tensile shear strength Al/Al [MPa] 55
DELO Standard 39, sand-blasted
component thickness: 6 mm
after 40 min at +150 °C
Floating roller peel resistance St/St [N/mm] 12
DELO Standard 38, sand-blasted
component thickness: 1.5 mm
Temperature stability Al/Al at +50 °C [MPa] 33
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mmm
Temperature stability Al/Al at +100 °C [MPa] 22
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mm
Temperature stability Al/Al at +150 °C [MPa] 5
according to DIN EN 1465, sand-blasted
component thickness: 1.6 mm
Tensile strength [MPa] 40
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Elongation at tear [%] 1.4
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Young’s modulus [MPa] 3300
according to DIN EN ISO 527
layer thickness: 2 mm
after 40 min at +150 °C
Shore hardness D 67
according to DIN EN ISO 868
after 40 min at +150 °C
Decomposition temperature [°C] 280
DELO Standard 36
Ball indentation hardness [MPa] 95
ISO 2039, part 1
Glass transition temperature [°C] 140
rheometer
Coefficient of linear expansion [ppm/K] 93
TMA, in a temperature range of +25 to +140 °C
Coefficient of linear expansion [ppm/K] 65
TMA, in a temperature range of +30 to +90 °C
Coefficient of linear expansion [ppm/K] 171
TMA, in a temperature range of +130 to +150 °C
Shrinkage [vol. %] 3.0
DELO Standard 13
Water absorption [weight %] 0.1
according to DIN EN ISO 62
after 40 min at +150 °C
Dielectric strength [kV/mm] 2
VDE 0303, part 2, after 40 min at +150 °C
Dielectric constant 3.6
VDE 0303, part 4, after 40 min at +150 °C
Creep resistance CTI 125M
VDE 0303, part 1, IEC 112, after 40 min at +150 °C
Storage life at 0 °C to +8 °C 6 months
in unopened original container
Instructions and advice
General
The data and information provided are based on tests performed under laboratory conditions. Reliable information about the behavior of the product under practical conditions and its suitability for a specific purpose cannot be concluded from this.
Many product properties are subject to temperature and may change permanently, especially at high temperatures.
It is the user’s responsibility to test the suitability of the product for the intended purpose and temperature range of use by considering all specific requirements. Type and physical and chemical properties of the materials to be processed with the product, as well as all actual influences occurring during transport, storage, processing and use, may cause deviations in the behavior of the product
compared to its behavior under laboratory conditions. All data provided are typical average values or uniquely determined parameters
measured under laboratory conditions.
The data and information provided are, therefore, no guarantee for specific product properties or the suitability of the product for a specific purpose.
Instructions for use
The instructions for use of DELOMONOPOX are available on: www.DELO.de. We will be pleased to send them to you on demand.
Occupational health and safety
see material safety data sheet
Specification
see quality assurance test report
华为网盘下载: http://dl.dbank.com/c0kpy24m9x
注册本地下载:
DELO_MONOPOX_1197 (167.0 KB, 7 次)
您没有权限下载此文件。
《【扒一扒】日本高纯球形硅微粉材料生产商》： 作为一种无机非金属矿物功能性粉体材料，硅微粉广泛应用于电子材料、电工绝缘材料、胶黏剂、特种陶瓷、精密铸造、油漆涂料、油墨、硅橡胶等领域。 目前，世界上只有中国、日本、韩国、美国等少数国家具备硅微粉生产能力... 全文 ?