PRODUCT DESCRIPTION

LOCTITE® HF8075LV™ provides  the following product characteristics

Technology Acrylic
Chemical Type Methacrylate
Appearance (Part A) Yellow paste
Appearance (Part B) Blue paste
Appearance (Mixture) Green pasteLMS
Cure Room temperature cure
Components Two component – requires mixing
Mix  Ratio,  by  volume – Part A: Part B 10 : 1
Product Benefits ●   Rapid room temperature cure●   Excellent bond strength
Application Bonding

LOCTITE® HF8075LV™ is a toughened, two component, room temperature curing methacrylate adhesive system. It is designed to comply with the low halogen content requirements for structural bonding of electronic assemblies. LOCTITE® HF8075LV™  cures  rapidly,  forming  tough,  resilient  bonds. Once statically mixed, the two component acrylic cures at room temperature. Cure times can be reduced with the addition of mild heat to the bonded assemblies. Typical applications include structural bonding of plastic and metal components that must withstand vibrations and impacts such as display, top case, structural frame to enclosure, and similar applications in the portable devices market.

TYPICAL PROPERTIES OF UNCURED MATERIAL

Part A:

Specific Gravity @ 25 °C                              1.03

Viscosity, Cone & Plate, 25 °C, mPa·s (cP):

Shear rate 36 s-1                                                            11,000 to 22,000LMS

Part B:

Specific Gravity @ 25 °C                              1.15

Viscosity, Cone & Plate, 25 °C, mPa·s (cP):

Shear rate 36 s-1                                                            10,000 to 20,000LMS

Mixed:

Working Time @ 25 °C, minutes

(maximum time before assembly):

Steel                                                                4

Aluminium                                                       4

Polyethylene                                                  4

Ionic Contaminants, ppm:

Chlorine                                                         ≤900LMS
Bromine                                                         ≤900LMS
Chlorides and Bromides                           ≤1,500LMS

TYPICAL CURING PERFORMANCE Fixture Time

Fixture time is defined as the time to develop a shear strength of 0.1 N/mm² .

Fixture Time, ISO 4587, seconds:

Grit Blasted Mild Steel                                   270 to 300

Peak Exotherm Temperature

Peak Exotherm Temperature, 10 gram mass:

Peak Temperature Time, minutes                  5

Peak Temperature, °C                                     125

TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties:

Glass Transition Temperature (Tg)              87

, ISO 11359-2, °C

Coefficient of Thermal Expansion, ISO 11359-2 K-1:

Pre Tg                                                            114×10-06

Post Tg                                                          206×10-06

Shore Hardness, ISO 868, Durometer D      67

Linear Shrinkage, ISO 1675 %                      5.8

Volume Shrinkage, ISO 1675 %                    16.6

Elongation, at break, ISO 527-2, %               167

Elongation, at yield, ISO 527-2, %                9

Tensile Strength, at yield, ISO527-2                        N/mm²    21

Tensile Strength, at break, ISO527-2                      N/mm²    20

Tensile Modulus, ISO 527-2                                     N/mm²    587

……

后面还有很多关于给种材质的粘接数据,不大好粘贴,大家可以直接下载PDF文件查看之!

 

华为网盘下载:http://dl.vmall.com/c0lee0dfij

注册本地下载:

  LOCTITE HF8075LV (66.3 KB, 11 次)
您没有权限下载此文件。

 

 

 

 

 

豆瓣 腾讯微博 QQ空间 新浪微博

电子胶水达人!

    联系站长

    • Name:QiuBo QQ:1808976
      Email:Anndiqiu#Gmail.com
      Mobile Phone:13923499497

    热门文章

    添加站长微信,与站长在线实时交流

    QQ不在线时请用微信

    最近评论

    • 正在加载...

    轻量、专注的消息,关注电子胶粘剂、电子胶水、电子制造工艺及设备产品的新鲜资讯。

链接