{"id":2808,"date":"2011-12-22T21:12:47","date_gmt":"2011-12-22T13:12:47","guid":{"rendered":"http:\/\/www.g4e.cn\/wordpress\/?p=2808"},"modified":"2013-11-19T15:38:46","modified_gmt":"2013-11-19T07:38:46","slug":"loctite-3106-uv-glue-tds","status":"publish","type":"post","link":"http:\/\/www.g4e.cn\/wordpress\/datasheet\/2808.html","title":{"rendered":"\u4e50\u6cf03106 UV\u80f6 TDS"},"content":{"rendered":"

\u8fd1\u65e5\u6709\u4e2a\u505a\u97f3\u5708\u7684\u5ba2\u6237\u4f7f\u7528\u4e50\u6cf03106\u505a\u4e2d\u5fc3\u80f6\u7528\u9014\uff0c\u636e\u53cd\u6620\u611f\u89c9\u7c98\u63a5\u529b\u4e0d\u592a\u591f\u800c\u4e14\u89c9\u5f97\u786c\u5ea6\u4e5f\u4e0d\u591f\u3002 \u7ed9\u5176\u63a8\u8350\u4e86\u4e24\u6b3e\u4ea7\u54c1\u91cd\u65b0\u5c1d\u8bd5\uff0c\u5728\u4e50\u6cf0\u5b98\u7f51\u4e0b\u8f7d\u4e86\u8fd9\u4efdTDS\u8d44\u6599\uff0c\u6458\u5f55\u5982\u4e0b\uff0c\u611f\u5174\u8da3\u7684\u670b\u53cb\u53ef\u4ee5\u53bb\u4e0b\u8f7dPDF\u7248\u672c\uff1a<\/p>\n

PRODUCT DESCRIPTION
\nLOCTITE\u00ae 3106\u2122 provides the following product
\ncharacteristics:
\nTechnology Acrylic
\nChemical Type Acrylated urethane
\nAppearance (uncured) Transparent liquidLMS
\nComponents One component – requires no mixing
\nViscosity Medium, thixotropic
\nCure Ultraviolet (UV)\/ visible light
\nCure Benefit Production – high speed curing
\nApplication Bonding
\nFlexibility Enhances load bearing & shock
\nabsorbing characteristics of the bond
\narea.
\nLOCTITE\u00ae 3106\u2122 is primarily designed for bonding rigid or
\nflexible PVC to polycarbonate where large gap filling
\ncapabilities and flexible joints are desired. The product has
\nshown excellent adhesion to a wide variety of substrates
\nincluding glass, many plastics and most metals. The thixotropic
\nnature of LOCTITE\u00ae 3106\u2122 reduces the migration of liquid
\nproduct after application to the substrate.
\nTYPICAL PROPERTIES OF UNCURED MATERIAL
\nSpecific Gravity @ 25 \u00b0C 1.08
\nRefractive Index 1.48
\nFlash Point – See MSDS
\nViscosity, Brookfield – RVT, 25 \u00b0C, mPa\u00b7s (cP):
\nSpindle 4, speed 20 rpm 3,500 to 7,500LMS
\nTYPICAL CURING PERFORMANCE
\nLOCTITE\u00ae 3106\u2122 can be cured by exposure to UV and\/or
\nvisible light of sufficient intensity. To obtain full cure on
\nsurfaces exposed to air, radiation @ 220 to 260 nm is also
\nrequired. The speed of cure will depend upon the UV intensity
\nand spectral distribution of the light source, the exposure time
\nand the light transmittance of the substrates.
\nStress Cracking
\nLiquid adhesive is applied to a polycarbonate bar 6.4 cm by
\n13 mm by 3 mm which is then flexed to induce a known stress
\nlevel.
\nStress Cracking, ASTM D 3929, minutes:
\n7 N\/mm\u00b2 stress on bar >15
\n12 N\/mm\u00b2 stress on bar 13 to 14<\/p>\n

Fixture Time
\nFixture time is defined as the time to develop a shear strength
\nof 0.1 N\/mm\u00b2.
\nUV Fixture Time, Glass microscope slides, seconds:
\nBlack light, Zeta\u00ae 7500 light source:
\n6 mW\/cm\u00b2, measured @ 365 nm \u226415LMS
\nUV Fixture Time, Polycarbonate to PVC, seconds:
\nMetal halide bulb, Zeta\u00ae 7400:
\n30 mW\/cm\u00b2, measured @ 365 nm, <5
\nElectrodeless, H & V bulbs:
\n50 mW\/cm\u00b2, measured @ 365 nm, <5
\nElectrodeless, D bulb:
\n50 mW\/cm\u00b2, measured @ 365 nm, <5
\nDepth of Cure vs. Irradiance (365 nm)
\nThe graph below shows the increase in depth of cure with time
\nat 50mW\/cm\u00b2 – 100mW\/cm\u00b2 as measured from the thickness
\nof the cured pellet formed in a 15mm diameter PTFE die.
\nNote: When exposed to a V Bulb at irradiances of 50 and 100
\nmW\/cm\u00b2 for 30 seconds, a depth of cure greater than 13 mm
\nwas achieved. The performance for medium pressure Hg will
\nbe similar to Electrodeless system, H bulb<\/p>\n

TYPICAL PROPERTIES OF CURED MATERIAL
\nCured @ 30 mW\/cm\u00b2, measured @ 365 nm, for 80 seconds using
\na glass filtered metal halide light source
\nPhysical Properties:
\nShore Hardness, ISO 868, Durometer D 53
\nRefractive Index 1.5
\nWater Absorption, ISO 62, %:
\n2 hours in boiling water 3.18
\nElongation, at break, ISO 527-3, % 250
\nTensile Modulus, ISO 527-3 N\/mm\u00b2 255
\n(psi) (37,000)
\nTensile Strength, at break, ISO 527-3 N\/mm\u00b2 18.6
\n(psi) (2,700)
\nElectrical Properties:
\nSurface Resistivity, IEC 60093, \u03a9\u2219cm 9.2\u00d71014
\nVolume Resistivity, IEC 60093, \u03a9\u00b7cm 7.7\u00d71014
\nDielectric Breakdown Strength, , kV\/mm 26
\nDielectric Constant \/ Dissipation Factor, IEC 60250:
\n100-Hz 5.17 \/ 0.04
\n1-kHz 5.01 \/ 0.02
\n1-MHz 4.61 \/ 0.04
\nTYPICAL PERFORMANCE OF CURED MATERIAL
\nAdhesive Properties
\nCured @ 30 mW\/cm\u00b2, measured @ 365 nm, for 80 seconds using
\na metal halide light source, (samples with 0.5 mm gap).
\nLap Shear Strength, ISO 4587:
\nPolycarbonate N\/mm\u00b2 *5.2
\n(psi) (750)
\n* substrate failure<\/p>\n

TYPICAL ENVIRONMENTAL RESISTANCE
\nCured @ 30 mW\/cm\u00b2, measured @ 365 nm, for 80 seconds using
\na metal halide light source, (samples with 0.5 mm gap).
\nLap Shear Strength, ISO 4587:
\nPolycarbonate:
\n0.5 mm gap
\nChemical\/Solvent Resistance
\nAged under conditions indicated and tested @ 22 \u00b0C.
\n% of initial strength
\nEnvironment \u00b0C 2 h 24 h 170 h
\nBoiling water 100 * 100 ——– ——–
\nWater immersion 49 * 100 ——– ——–
\nWater immersion 87 * 100 ——– ——–
\nIsopropanol immersion 22 ——– 95 ——–
\nHeat\/humidity 38 ——– ——– * 100
\nHeat Aging
\nLap Shear Strength, ISO 4587, % of initial strength:
\nPolycarbonate:
\nAged @ 71 \u00b0C for 170 hours *100
\nAged @ 71 \u00b0C for 340 hours *100
\nAged @ 93 \u00b0C for 170 hours *100
\nAged @ 93 \u00b0C for 340 hours *100
\n* substrate failure
\nGENERAL INFORMATION
\nThis product is not recommended for use in pure oxygen
\nand\/or oxygen rich systems and should not be selected as
\na sealant for chlorine or other strong oxidizing materials.
\nFor safe handling information on this product, consult the
\nMaterial Safety Data Sheet (MSDS).
\nWhere aqueous washing systems are used to clean the
\nsurfaces before bonding, it is important to check for
\ncompatibility of the washing solution with the adhesive. In
\nsome cases these aqueous washes can affect the cure and
\nperformance of the adhesive.
\nThis product is not normally recommended for use on plastics
\n(particularly thermoplastic materials where stress cracking of
\nthe plastic could result). Users are recommended to confirm
\ncompatibility of the product with such substrates.
\nDirections for use
\n1. This product is light sensitive; exposure to daylight, UV
\nlight and artificial lighting should be kept to a minimum
\nduring storage and handling.
\n2. The product should be dispensed from applicators with
\nblack feedlines.
\n3. For best performance bond surfaces should be clean and
\nfree from grease.
\n4. Cure rate is dependent on lamp intensity, distance from
\nlight source, depth of cure needed or bondline gap and
\nlight transmittance of the substrate through which the
\nradiation must pass.
\n5. Recommended intensity for cure in bondline situation is 5
\nmW\/cm\u00b2 minimum (measured at the bondline) with an
\nexposure time of 4-5 times the fixture time at the same
\nintensity.<\/p>\n

6. For dry curing of exposed surfaces, higher intensity UV is
\nrequired (100 mW\/cm\u00b2).
\n7. Cooling should be provided for temperature sensitive
\nsubstrates such as thermoplastics.
\n8. Crystalline and semi-crystalline thermoplastics should be
\nchecked for risk of stress cracking when exposed to liquid
\nadhesive.
\n9. Excess adhesive can be wiped away with organic solvent.
\n10. Bonds should be allowed to cool before subjecting to any
\nservice loads.
\nLoctite Material SpecificationLMS
\nLMS dated April-22, 2002. Test reports for each batch are
\navailable for the indicated properties. LMS test reports include
\nselected QC test parameters considered appropriate to
\nspecifications for customer use. Additionally, comprehensive
\ncontrols are in place to assure product quality and
\nconsistency. Special customer specification requirements may
\nbe coordinated through Henkel Quality.
\nStorage
\nStore product in the unopened container in a dry location.
\nStorage information may be indicated on the product container
\nlabeling.
\nOptimal Storage: 8 \u00b0C to 21 \u00b0C. Storage below 8 \u00b0C or
\ngreater than 28 \u00b0C can adversely affect product properties.
\nMaterial removed from containers may be contaminated during
\nuse. Do not return product to the original container. Henkel
\nCorporation cannot assume responsibility for product which
\nhas been contaminated or stored under conditions other than
\nthose previously indicated. If additional information is required,
\nplease contact your local Technical Service Center or
\nCustomer Service Representative.
\nConversions
\n(\u00b0C x 1.8) + 32 = \u00b0F
\nkV\/mm x 25.4 = V\/mil
\nmm \/ 25.4 = inches
\n\u03bcm \/ 25.4 = mil
\nN x 0.225 = lb
\nN\/mm x 5.71 = lb\/in
\nN\/mm\u00b2 x 145 = psi
\nMPa x 145 = psi
\nN\u00b7m x 8.851 = lb\u00b7in
\nN\u00b7m x 0.738 = lb\u00b7ft
\nN\u00b7mm x 0.142 = oz\u00b7in
\nmPa\u00b7s = cP<\/p>\n

 <\/p>\n

\u70b9\u51fb\u4e0b\u8f7dPDF\u6587\u4ef6\uff1a

\"\"  loctite 3106 TDS<\/strong> (66.4 KB, 6 \u6b21)
\u60a8\u6ca1\u6709\u6743\u9650\u4e0b\u8f7d\u6b64\u6587\u4ef6\u3002<\/i><\/p><\/p>\n","protected":false},"excerpt":{"rendered":"

\u8fd1\u65e5\u6709\u4e2a\u505a\u97f3\u5708\u7684\u5ba2\u6237\u4f7f\u7528\u4e50\u6cf03106\u505a\u4e2d\u5fc3\u80f6\u7528\u9014\uff0c\u636e\u53cd\u6620\u611f\u89c9\u7c98\u63a5\u529b\u4e0d\u592a\u591f\u800c\u4e14\u89c9\u5f97\u786c\u5ea6\u4e5f\u4e0d\u591f\u3002 \u7ed9\u5176\u63a8\u8350\u4e86\u4e24\u6b3e\u4ea7 […]<\/p>\n","protected":false},"author":1,"featured_media":3732,"comment_status":"open","ping_status":"open","sticky":false,"template":"","format":"standard","meta":[],"categories":[667],"tags":[486,456,485],"_links":{"self":[{"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/posts\/2808"}],"collection":[{"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/posts"}],"about":[{"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/types\/post"}],"author":[{"embeddable":true,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/users\/1"}],"replies":[{"embeddable":true,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/comments?post=2808"}],"version-history":[{"count":0,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/posts\/2808\/revisions"}],"wp:featuredmedia":[{"embeddable":true,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/media\/3732"}],"wp:attachment":[{"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/media?parent=2808"}],"wp:term":[{"taxonomy":"category","embeddable":true,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/categories?post=2808"},{"taxonomy":"post_tag","embeddable":true,"href":"http:\/\/www.g4e.cn\/wordpress\/wp-json\/wp\/v2\/tags?post=2808"}],"curies":[{"name":"wp","href":"https:\/\/api.w.org\/{rel}","templated":true}]}}